DU Wei
,
et al
钢铁研究学报(英文版)
The microstructure, texture and formability of Nb+Ti stabilized high-purity ferritic stainless steel were investigated. The interstitial elements C and N could be fully stabilized with Nb and Ti, and the precipitates were mainly composed of TiN and NbC. By analyzing texture at the various thermomechanical processes, the intensity of α-fiber obtained during hot rolling was reduced greatly after annealing and a non-uniform γ-fiber was achieved. The favorable γ-fiber was displayed in cold rolled and annealed sheet, whereas the texture maximum located at (554)<225>. The formation of this shifted texture mainly attributed to the influence of “Zener” drag and selective growth. Finally, the obtained mean r-value was notably higher, mean r=1.70, compared with traditional ferritic stainless steels.
关键词:
texture;microstructure;formability;dual stabilization